Vitralit® 2009 F is a combined cationic UV- and thermally curable coating
compound, based on epoxies. The surface is dry after the UV curing process,
stability will be reached, once the coating has cooled down. Deep layers or
shadowed areas can be post cured thermally. Vitralit® 2009 F is a flexible
coating, can be autoclaved and is highly chemical resistant.
Technical Data- Color: transparent
- Viscosity [mPa*s]: 100 to 200
- Flash point [°C]: > 100
- Full Strength [hours]: 24
- Temperature Resistance [°C]: -40 to 180
- Hardness Shore D: 40 to 50
- Compression Shear Strength (PC/PC) [MPa]: 1,2
- Compression Shear Strength (PC/PMMA) [MPa]: 1,7
- Compression Shear Strength (PMMA/FR4) [MPa]: 2,1
- Lap Shear Strength (PMMA/Glass) [MPa]: 2,8
- Lap Shear Strength (Glass/PC) [MPa]: 2,6
- Lap Shear Strength (Glass/Glass) [MPa]: 4,7
- Elongation at Break [%]: 210