Typical properties | |
Recommended dry film thickness: | 500 microns |
Theoretical coverage with Recommended DFT: | 1,2 m2/L |
Cure time at 20°C: | 24 hours |
Technical properties at 20°C | |
Density: | 1,3 kg/L |
Viscosity; Brookfield with 20 RPM: | 18000 mPa.s |
pH: | 8,5 |
Non Volatile: | 70 weight-% |
Volatile organic compund content: ISO 11890-2 (10.4) | 2 g/L |
Accelerated corrosion tests with average recommended DFT | |
Salt Spray; 5% NaCl at 35°C: ISO 9227 NSS (Cold rolled polished steel panels, acc. to SAE 1010) | 21+ days |
Humidity; 100% RH at 40°C: ISO 6270-2 CH (Cold rolled polished steel panels, acc. to SAE 1010) | 21+ days |
Stone Chipping Resistance (Erichsen VDA 508) | ≥ 20 kg |
Fire Resistance (FMVSS 302) | 0 mm/min |